• español
  • English
  • français
  • Deutsch
  • português (Brasil)
  • italiano
    • español
    • English
    • français
    • Deutsch
    • português (Brasil)
    • italiano
    • español
    • English
    • français
    • Deutsch
    • português (Brasil)
    • italiano
    JavaScript is disabled for your browser. Some features of this site may not work without it.

    Listar

    Todo UVaDOCComunidadesPor fecha de publicaciónAutoresMateriasTítulos

    Mi cuenta

    Acceder

    Estadísticas

    Ver Estadísticas de uso

    Compartir

    Ver ítem 
    •   UVaDOC Principal
    • PRODUCCIÓN CIENTÍFICA
    • Departamentos
    • Dpto. Ciencia de los Materiales e Ingeniería Metalúrgica, Expresión Gráfica en la Ingeniería, Ingeniería Cartográfica, ..
    • DEP07 - Artículos de revista
    • Ver ítem
    •   UVaDOC Principal
    • PRODUCCIÓN CIENTÍFICA
    • Departamentos
    • Dpto. Ciencia de los Materiales e Ingeniería Metalúrgica, Expresión Gráfica en la Ingeniería, Ingeniería Cartográfica, ..
    • DEP07 - Artículos de revista
    • Ver ítem
    • español
    • English
    • français
    • Deutsch
    • português (Brasil)
    • italiano

    Exportar

    RISMendeleyRefworksZotero
    • edm
    • marc
    • xoai
    • qdc
    • ore
    • ese
    • dim
    • uketd_dc
    • oai_dc
    • etdms
    • rdf
    • mods
    • mets
    • didl
    • premis

    Citas

    Por favor, use este identificador para citar o enlazar este ítem:http://uvadoc.uva.es/handle/10324/21910

    Título
    Abnormal magnetic behaviour of powder metallurgy austenitic stainless steels sintered in nitrogen
    Autor
    García Cabezón, Ana CristinaAutoridad UVA Orcid
    Martín Pedrosa, FernandoAutoridad UVA Orcid
    Blanco Val, María YolandaAutoridad UVA Orcid
    Año del Documento
    2009
    Editorial
    ELSERVIER
    Documento Fuente
    Journal of Magnetism and Magnetic Materials 2009, 321, 3171–3177
    Resumen
    The magnetic response of AISI 304L and AISI 316L obtained through powder metallurgy and sintered in nitrogen were studied. AISI 304L sintered in nitrogen showed a ferromagnetic behaviour in as-sintered state while AISI 316L was paramagnetic. After solution annealing both were paramagnetic. Magnetic behaviour was analysed by using a vibrating sample magnetometer, a magnetic ferritscope and magnetic etching. A microstructural characterization was performed by means of optical metallography, X-ray diffraction, scanning electron microscopy (SEM) and energy dispersive analysis of X-rays (EDS). Some samples when needed were submitted to aged heat treatments at 675 and 875 °C for 90 min, 4, 6, 8 or 48 h. The main microstructural feature found was the presence of a lamellar constituent formed by nitride precipitates and an interlamellar matrix of austenite and/or ferrite. The abnormal magnetic response was explained based on this.
    Materias (normalizadas)
    Magnetic measurement
    Powder metallurgy
    Austenitic stainless steel
    ISSN
    0304-8853
    Revisión por pares
    SI
    DOI
    10.1016/j.jmmm.2009.05.025
    Patrocinador
    Dirección General de Programas y Transferencia de Conocimiento, Ministerio de Ciencia e Innovación, España, MAT2008-02788
    Propietario de los Derechos
    ELSERVIER
    Idioma
    eng
    URI
    http://uvadoc.uva.es/handle/10324/21910
    Derechos
    openAccess
    Aparece en las colecciones
    • DEP07 - Artículos de revista [51]
    Mostrar el registro completo del ítem
    Ficheros en el ítem
    Nombre:
    JOMM 321 (2009) 3171-3177.pdf