The role of defects in the resistive switching behavior of Ta2O5-TiO2-based metal–insulator–metal (MIM) devices for memory applications
Autor
Año del Documento
2018
Editorial
Springer Link
Descripción
Producción Científica
Documento Fuente
Journal of Electronic Materials, 2018, vol. 47, n. 9. p. 4938-4943
Zusammenfassung
We describe the role of defects in the resistive switching behavior of metal–insulator–metal devices based on alternating Ta2O5 and TiO2 stacks. Ruthenium oxide (RuOx) and platinum (Pt) were used as bottom and top electrodes, respectively. Insulator stacks with thickness of 5 nm were fabricated by atomic layer deposition of alternating Ta2O5 and TiO2 thin films. Bipolar resistive switching behavior was obtained for Ta2O5-TiO2-Ta2O5 and TiO2-Ta2O5-TiO2 stacks, being mainly due to presence of oxygen vacancy defects. The best memristive response was obtained in the case of two TiO2 films embedding a monolayer of Ta2O5. Highly repeatable direct-current (DC)-voltage bipolar switching cycles were obtained. Small-signal admittance parameters also showed hysteretic behavior during a whole bipolar switching cycle. In the case of samples with three layers of similar thickness, when the transition from ON to OFF state (reset) occurred, the conductance abruptly increased and the susceptance decreased quickly for more negative voltages values. Such behavior was not observed when only one Ta2O5 monolayer was examined. These differences can be explained in terms of the charge transport mechanism occurring in the open conductive filaments.
Palabras Clave
Resistive switching
Conmutación resistiva
Tantalum oxide
Pentóxido de tántalo
Titanium oxide
Óxido de titanio
ISSN
1543-186X
Revisión por pares
SI
Patrocinador
Ministerio de Economía, Industria y Competitividad (project TEC2014- 52152-C3-3-R)
Estonian Research Agency (projects PRG4 and IUT2-24)
Fondo Europeo de Desarrollo Regional (projects TK134 and TK141)
Estonian Research Agency (projects PRG4 and IUT2-24)
Fondo Europeo de Desarrollo Regional (projects TK134 and TK141)
Version del Editor
Propietario de los Derechos
© 2018 Springer
Idioma
eng
Tipo de versión
info:eu-repo/semantics/draft
Derechos
openAccess
Aparece en las colecciones
- Untitled [57]
Dateien zu dieser Ressource
![Attribution-NonCommercial-NoDerivatives 4.0 Internacional](/themes/Mirage2//images/creativecommons/cc-by-nc-nd.png)