Título: Tribocorrosion behaviour of powder metallurgy duplex stainless steels sintered innitrogen
Autor: Martín Pedrosa, Fernando
García Cabezón, Cristina
Blanco Val, Yolanda
Lopez Aparicio, Manuel
Año del Documento: 2013
Editorial: ELSERVIER
Documento Fuente: Tribology International (2013) 57 76–85
Resumen: The combined corrosion–wear of powder metallurgy duplex stainless steels obtained by the mixing of ferritic and austenitic powders in several proportions was studied. All the materials were sintered in a nitrogen atmosphere. Tribological and tribocorrosion behaviour was analyzed using a pin-on-disc. Electrochemical techniques: open circuit potential measurements, potentiodynamic polarization measurements and potentiostatic measurements at passive potential under sliding conditions were used. The obtained results were interpreted and related to microstructural features. The tribocorrion behaviour for powder metallurgy duplex stainless steels was a function of the applied electrochemical potential.
Materias (normalizadas): Sliding
Wear
Corrosive
Powder
ISSN: 0301-679X
Revisión por Pares: SI
DOI: http://dx.doi.org/10.1016/j.triboint.2012.06.032
Patrocinador: Ministerio de Ciencia e Innovación, Dirección General de Programas yTransferencia de Conocimiento, Proyectos I+D, MAT2008-02788
Propietario de los Derechos: ELSERVIER
Idioma: eng
URI: http://uvadoc.uva.es/handle/10324/21876
Derechos: info:eu-repo/semantics/embargoedAccess
Embargado hasta2030-01-01
Aparece en las colecciones:DEP07 - Artículos de revista

Ficheros en este ítem:
Fichero Descripción TamañoFormato 
ártículo 2013.pdf2,07 MBAdobe PDFVisualizar/Abrir


Los ítems de UVaDOC están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.

Comentarios
Universidad de Valladolid
Powered by MIT's. DSpace software, Version 5.5