• español
  • English
  • français
  • Deutsch
  • português (Brasil)
  • italiano
    • español
    • English
    • français
    • Deutsch
    • português (Brasil)
    • italiano
    • español
    • English
    • français
    • Deutsch
    • português (Brasil)
    • italiano
    JavaScript is disabled for your browser. Some features of this site may not work without it.

    Listar

    Todo UVaDOCComunidadesPor fecha de publicaciónAutoresMateriasTítulos

    Mi cuenta

    Acceder

    Estadísticas

    Ver Estadísticas de uso

    Compartir

    Ver ítem 
    •   UVaDOC Principal
    • PRODUCCIÓN CIENTÍFICA
    • Grupos de Investigación
    • Materiales Magnéticos
    • MM - Artículos de Revista
    • Ver ítem
    •   UVaDOC Principal
    • PRODUCCIÓN CIENTÍFICA
    • Grupos de Investigación
    • Materiales Magnéticos
    • MM - Artículos de Revista
    • Ver ítem
    • español
    • English
    • français
    • Deutsch
    • português (Brasil)
    • italiano

    Exportar

    RISMendeleyRefworksZotero
    • edm
    • marc
    • xoai
    • qdc
    • ore
    • ese
    • dim
    • uketd_dc
    • oai_dc
    • etdms
    • rdf
    • mods
    • mets
    • didl
    • premis

    Citas

    Por favor, use este identificador para citar o enlazar este ítem:http://uvadoc.uva.es/handle/10324/40723

    Título
    Broadband transverse susceptibility in multiferroic Y-type hexaferrite Ba0.5Sr1.5Zn2Fe12O22
    Autor
    Hernández Gómez, PabloAutoridad UVA
    Martín González, D.
    Torres Cabrera, CarlosAutoridad UVA Orcid
    Muñoz Muñoz, José MaríaAutoridad UVA
    Año del Documento
    2020
    Editorial
    Elsevier
    Descripción
    Producción Científica
    Documento Fuente
    Journal of Magnetism and Magnetic Materials Volume 506, 2020, 166808
    Resumen
    Noncollinear spin systems with magnetically induced ferroelectricity from changes in spiral magnetic ordering have attracted significant interest in recent research due to their remarkable magnetoelectric effects with promising applications. Single phase multiferroics are of great interest for these new multifunctional devices, being Y-type hexaferrites good candidates, and among them the ZnY compounds due to their ordered magnetic behaviour over room temperature. Polycrystalline Y type hexaferrites with composition Ba0.5Sr1.5Zn2Fe2O22 (BSZFO) were sintered in 1050 °C–1250 °C temperature range. Transverse susceptibility measurements carried out on these BSZFO samples in the temperature range 80–350 K with DC fields up to ± 5000 Oe reveal different behaviour depending on the sintering temperature. Sample sintered at 1250 °C is qualitatively different, suggesting a mixed Y and Z phase like CoY hexaferrites. Sintering at lower temperatures produce single phase Y-type, but the transverse susceptibility behaviour of the sample sintered at 1150 °C is shifted at temperatures 15 K higher. Regarding the DC field sweeps the observed behaviour is a peak that shifts to lower values with increasing temperature, and the samples corresponding to single Y phase exhibit several maxima and minima in the 250 K–330 K range at low DC applied field as a result of the magnetic field induced spin transitions in this compound.
    Palabras Clave
    Y-type hexaferrites
    Hexaferritas de tipo Y
    Multiferroic materials
    Materiales multiferroicos
    Transverse susceptibility
    ISSN
    0304-8853
    Revisión por pares
    SI
    DOI
    10.1016/j.jmmm.2020.166808
    Patrocinador
    Ministerio de Ciencia, Innovación y Universidades; Agencia Estatal de Investigación with FEDER (MAT2016-80784-P)
    Version del Editor
    https://authors.elsevier.com/a/1aq1I15KgbA05H
    Propietario de los Derechos
    © 2020 Elsevier
    Idioma
    eng
    URI
    http://uvadoc.uva.es/handle/10324/40723
    Tipo de versión
    info:eu-repo/semantics/submittedVersion
    Derechos
    openAccess
    Aparece en las colecciones
    • DEP22 - Artículos de revista [65]
    • MM - Artículos de Revista [8]
    Mostrar el registro completo del ítem
    Ficheros en el ítem
    Nombre:
    manuscript_phg_jems2019_preprint.pdf
    Tamaño:
    721.5Kb
    Formato:
    Adobe PDF
    Thumbnail
    Visualizar/Abrir
    Attribution-NonCommercial-NoDerivatives 4.0 InternacionalLa licencia del ítem se describe como Attribution-NonCommercial-NoDerivatives 4.0 Internacional

    Universidad de Valladolid

    Powered by MIT's. DSpace software, Version 5.10